Gnu.

5K views 13 replies 5 participants last post by  blunted_nose 
#1 ·
How bad is the partial edge design? Does it justify the need to buy something else? Am i screwed, as my last board had full edges and the nose and tail are pretty wrecked... Why in the world wouldnt they just make it full edge wraping and forget about that extra half a pound.
 
#2 ·
Wavy edges are a pain to lay by hand, doing a full wrap with wavy is even harder. Saves a boat load of time to tuck edges, saving time is saving money. They use a deeper than average tip fill to "protect" the wood core but if you bang up tips a lot you have a fair enough chance to rip out an edge and an even better chance to peel the topsheet. A pulled edge can be somewhat fixed by a good tech, topsheet peels are "fixable" with epoxy but it will never be as good as new.

That's only one reason I can give you as to why any Gnu/Lib should not be a top choice though... I could rant...
 
#3 ·
Wavy edges are a pain to lay by hand, doing a full wrap with wavy is even harder. Saves a boat load of time to tuck edges, saving time is saving money. They use a deeper than average tip fill to "protect" the wood core but if you bang up tips a lot you have a fair enough chance to rip out an edge and an even better chance to peel the topsheet. A pulled edge can be somewhat fixed by a good tech, topsheet peels are "fixable" with epoxy but it will never be as good as new.

That only one reason I can give you as to why any Gnu/Lib should not be a top choice though... I could rant...
Could this justify getting a new board, I bought it like 3 days ago, i can still return, but my only other option is to buy a burton. I paid 350, but the boards go for 600, at that price i cant imagine that you can break them easy. Im not hitting park! The heck with it, im going to take care of it, if it break im going to fix it, if it break easy im going to fix it and never going to buy another mervin board. I wish i could get a jones or the new slash by Gigi ruf.
 
#7 ·
What did you get, and where are you riding? If you deal with shit snow 40% or less (like you're in Utah or Colorado or Wyoming...) then the Sherlock is an amazing in bounds powder board.
Haa canada here, so all natural big mtn riding. I got a billy goat 162! But i heard that burton top sheet cracks and im not Too fond of est, as it limits me to burton only board.
 
#8 ·
Haa canada here, so all natural big mtn riding. I got a billy goat 162! But i heard that burton top sheet cracks and im not Too fond of est, as it limits me to burton only board.
Nearly every binding manufacturer makes M6 conversion now so you're not locked into Burton bindings. Even though the Malavitas are super rad anyhow, the hinge rules. They'd match super well with the Sherlock.

If you're all mountainy I'd switch for a Sherlock. If you're freeridey this is one of the rare cases I'd say Gnu. Just cause I'd rather see you keep your money at your local shop than find something online. It's by no means a terrible board, just not worth the $600 or so they ask full price. When it really comes down to it a board choice is not as important as we make it out to be. Don't get a jibstick to drop cliffs or a cliff dropper to slide metal and you're probably going to have fun as long as you don't over think your stick. Some of my all time best pow days have been on complete jib sticks. One was upper side of Breck in Lake Chutes on my Nitro Subzero and the other was mobbing around the backside of Keystone on my jib sized Signal Park. Your riding is more important that your board.

I don't remember anything major about peeling topsheets on Burtons. If there was something it was likely a factory problem on a certain model. Nothing I would worry about.
 
#10 ·
Hi Blunted,

Here is something I wrote for our first shop back in the early 90's. This debate has been going on for a while :)

Don't spend too much time debating tip and tail construction:

Many first time buyers become focused on the differences between manufacturer's approaches towards tip and tail construction. Some brands argue that wood in the ends is the way to go for a consistent flex pattern. Others state that you need fiberglass for low swing weight. Some argue that extra metal edge should be laid in, to protect from damage, while others feel this added weight is unacceptable. Truth is, it really doesn't matter much at all. First off, most boards are damaged in the pickup on the way up the hill or by trying to jam the tail into snow that turns out not to be snow on the way in to grab a burger, or by the baggage handlers at La Guardia. No type of end structure will prevent against this. Metal edges all around, when struck hard, often wedge themselves into the board, creating more damage than had they not been there. On the other hand, the weight of the small amount of metal added, can barely be felt by even the most seasoned rider. Similarly, wood in the tip, adds almost no weight, but doesn't really enhance the ride either. The downside of having wood to the end is that if the board does sustain edge damage to the core, the wood will absorb moisture and is much trickier to fix. The bottom line is, be careful with whatever board you choose, and don't let this be the deciding factor.
 
#11 ·
This is actually killing me in my mind. Does anyone also overthink everything? Its like i make myself think my board is fine, BUT i can never trust my judgment, Eh its hard to explain. No matter what anyone is going to say, ill keep thinking i have the wrong board, The fact is that once on snow those tought's will disapear and ill be good. I just need it to snow right now.
 
#12 ·
Crazy overanalysis my friend.

I have a 2 year old billy goat with Co2's(IMO the best B binding of all time) that
i've ridden all over the country from near blizzard tree riding/hike-to at wolf creek to the hellish carnage know as the backside of Vail in the shitty ice last winter.

It looks no different wear and tear wise than any of my other boards.

Go out and enjoy the BG, it's a great deck that's not as stiff or as serious as most think.
It has a fast base, mellow mag that holds a great line, a relatively narrow ww that allows you to go edge to edge quickly, and it's damp.
Also slays Pow.

Great board, great purchase.
Oh, and it's added bonus if you get the graphic on mine(its going on the wall when I retire it)
 